432.  The effect of heat in increasing the conducting power of many substances, especially for electricity of high tension, is well known.  I have lately met with an extraordinary case of this kind, for electricity of low tension, or that of the voltaic pile, and which is in direct contrast with the influence of heat upon metallic bodies, as observed and described by Sir Humphry Davy[A].

  [A] Philosophical Transactions, 1821, p. 131.

433.  The substance presenting this effect is sulphuret of silver.  It was made by fusing a mixture of precipitated silver and sublimed sulphur, removing the film of silver by a file from the exterior of the fused mass, pulverizing the sulphuret, mingling it with more sulphur, and fusing it again in a green glass tube, so that no air should obtain access during the process.  The surface of the sulphuret being again removed by a file or knife, it was considered quite free from uncombined silver.

434.  When a piece of this sulphuret, half an inch in thickness, was put between surfaces of platina, terminating the poles of a voltaic battery of twenty pairs of four-inch plates, a galvanometer being also included in the circuit, the needle was slightly deflected, indicating a feeble conducting power.  On pressing the platina poles and sulphuret together with the fingers, the conducting power increased as the whole became warm.  On applying a lamp under the sulphuret between the poles, the conducting power rose rapidly with the heat, and at last-the galvanometer needle jumped into a fixed position, and the sulphuret was found conducting in the manner of a metal.  On removing the lamp and allowing the heat to fall, the effects were reversed, the needle at first began to vibrate a little, then gradually left its transverse direction, and at last returned to a position very nearly that which it would take when no current was passing through the galvanometer.

435.  Occasionally, when the contact of the sulphuret with the platina poles was good, the battery freshly charged, and the commencing temperature not too low, the mere current of electricity from the battery was sufficient to raise the temperature of the sulphuret; and then, without any application of extraneous heat, it went on increasing conjointly in temperature and conducting power, until the cooling influence of the air limited the effects.  In such cases it was generally necessary to cool the whole purposely, to show the returning series of phenomena.

436.  Occasionally, also, the effects would sink of themselves, and could not be renewed until a fresh surface of the sulphuret had been applied to the positive pole.  This was in consequence of peculiar results of decomposition, to which I shall have occasion to revert in the section on Electro-chemical Decomposition, and was conveniently avoided by inserting the ends of two pieces of platina wire into the opposite extremities of a portion of sulphuret fused in a glass tube, and placing this arrangement between the poles of the battery.